- 2024-06-13jewelleryz
0CrMoA合金管含碳0.26~0.34,硅0.17~0.37,锰0.40~0.70,钼0.15~0.25,铬0.80~1.10,A级 标准:GB/T 3077-1988① 钢号开头的两位数字表示钢的碳含量,以平均碳含量的万分之几
赞59
![](http://static-xiaoguotu.17house.com/zt/style/pc/user_logo/e645277b7163b2ca5b38d0f5f534647ba6d413d7.jpg)
- 2024-06-13赤影妖妖艾可
管含碳0.26~0.34,硅0.17~0.37,锰0.40~0.70,钼0.15~0.25,铬0.80~1.10,
赞105
![](http://static-xiaoguotu.17house.com/zt/style/pc/user_logo/e600a1d729ebc5572ed4b6445011c54b507a2971.jpg)
- 2024-06-13蝴蝶圆舞曲
30CrMoA30CrMoA化学成分:碳 C :0.26~0.34 硅 Si:0.17~0.37 锰 Mn:0.40~0.70 硫 S :允许残余含量≤0.025 磷 P :允许残余含量≤0.025 铬 Cr:0.80~1.10 镍 Ni:允许残余含量≤0.030 铜 Cu:允许残余
赞119
![](http://static-xiaoguotu.17house.com/zt/style/pc/user_logo/3da6db9791f6236931a17e56e5f02c262b0687cd.jpg)
- 2024-06-13齐吃大乳
30crmoa合金钢参数:
抗拉强度 σb (MPa):≥930(95)
屈服强度 σs (MPa):≥735(75)
伸长率 δ5 (%):≥12
断面收缩率 ψ (%):≥50
冲击功 Akv (J):≥71
冲击韧性值 αkv (J/cm2):≥88(9)
硬度 :≤229HB
赞209
![](http://static-xiaoguotu.17house.com/zt/style/pc/user_logo/6f93509bcf61542a4139d54fb47cf7eae6106ecc.jpg)
- 2024-06-13yannychan108
通常α合金和(α+β)合金退火温度选在(α+β)—→β相转变点以下120~200℃;固溶和时效处理是从高温区快冷,以得到马氏体α′相和亚稳定的β相,然后在中温区保温使这些亚稳定相分解,得到α相或化合物等细小弥散的第二相质点,达到使合金强化的目的。通常(α+β)合金的淬火在(α+β)—→β相转变点以下40~100℃进行,亚稳定β合金淬火在(α+β)—→β相转变点以上40~80℃进行。时效处理温度一般为450~550℃。此外,为了满足工件的特殊要求,工业上还采用双重退火、等温退火、β热处理、形变热处理等金属热处理工艺。